Plunkett Associates believe aluminium tooling offers significant benefits in the right applications.
1. Being a softer metal, it is faster to machine. This can have price benefits and result in faster delivery times.
2. Aluminium has a better thermal conductivity than steel, with the potential therefore to offer reduced cycle times.
3. For high gloss finishes, it can be polished about 30% faster.
Commonly asked questions:
Is aluminium a good material to use as a mould tool?
First and foremost it is important that we are talking tooling grade aluminium, 7000 series or higher. Softer grades will only survive very short runs and are frequently behind the bad stories that people recite.
Ask any moulder about aluminium and tooling, and they will all acknowledge that aluminum being softer than the more traditional tool steels requires a little more attention. It is therefore important to always use a moulder who has experience with aluminium tools, in order that the moulds are looked after.
Alongside this, it is imperative that the mould is designed and built properly for effective moulding, which will in turn prolong the life of the tool.
How long will an aluminum tool last?
Some tools still run with well over 100,000 shots on them. However, the criteria for aluminum tooling is changing; in the past it tended to be used only for prototype tooling. You would get 50, 100 maybe 1,000 parts to be used for testing etc and you would then build a steel tool for the production parts.
Today aluminum tools are being used for 50,000, 100,000+ shots for production on occasions. Modern surface coatings can also be applied that will extend the aluminum tool life.
The key to longevity is the moulded material, start adding fillers like glass and the associated tool maintenance will increase, especially in high wear areas like the gates.
What are the best applications to use an aluminium tool for?
Certainly less complicated parts, point of sale and parts that use a non-abrasive material like a polypropylene or a TPE, work well with aluminum tools. Higher volumes using more abrasive materials (e.g. glass-filled, ABS) will obviously have a negative impact and shorten the length of the tool life.
What are the surface finish implications of using an aluminium tool?
Most surface finishes can be re created on an aluminium tool. However textured finishes will not last as long and its best to allow for an increased amount of draft to help with this.
Can you expect the same features using an aluminium tool, as you would do with a steel tool?
Usually yes, although some small features may well require inserting in steel to ensure a reasonable life.
How long does it take to make an aluminium tool?
How long is a piece of string?! This obviously depends on the complexity of the parts, however a simple tool can be produced in a couple of days, whereas more complex tools will require several weeks.
Who owns the tool once it is made?
The tool remains the property of the client once it has been made unless otherwise arranged. Exceptions to this are where MUD frames (fixed bolsters with interchangeable mould inserts), in which case the client would own the inserts only. Plunkett Associates take responsibility for the storage and maintenance of the tool on behalf of the client.
Can parts be overmoulded with an aluminium tool?
Yes, we would first mould a rigid plastic substrate, then a soft rubber or TPE would be moulded onto or around the substrate. This is often used for products that need a soft grip area to a rigid part.
Do you know a toolmaker who is experienced in making aluminium tools?
Yes, Plunkett Associates have trusted suppliers in the UK. If tooling is originating from the Far East, then we would source steel tools as controlling the grade of aluminium used can prove challenging! See our articles “Did you know we have a new local CNC machinist who specialises in aluminium?” and “Is using a Chinese supplier a viable solution for my project?” for more information.